Polyurethaansystemen voor schokdempermat
Ontvang de meest recente Prijsbetaling Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. orde: | 1000 Kilogram |
vervoer: | Ocean |
Haven: | SHANGHAI |
betaling Type: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. orde: | 1000 Kilogram |
vervoer: | Ocean |
Haven: | SHANGHAI |
Model: XC-7160/XC-8260
merk: Xuchuan
Plaats Van Herkomst: China
Types Van: Synthetische hars en kunststoffen
Code: XC-7160/XC-8260
Application: Cold resistance medium hardness sole,marine fender,shock absorption
Characteristic: Cold resistance medium hardness sole,marine fender, shock absorption after coating
Appearance: liquid
Verkoopeenheden | : | Kilogram |
Pakkettype | : | 20 & 225 kg/drum |
Afbeeldingsvoorbeeld | : | |
Download | : |
PRODUCT BESCHRIJVING
XC-7160/XC-8260 Polyurethaan Sytem voor schokdempermat
Schokabsorptiemat grondstoffen
Het PU -systeem voor schoenzolen wordt gekenmerkt door zijn duurzaamheid, flexibiliteit en uitstekende dempingseigenschappen. Het biedt langdurig comfort en ondersteuning, waardoor het ideaal is voor atletisch en dagelijks schoenen.
Polyurethaansysteem voor schokabsorptie, mat
A/B Materials Temperatures(℃) | 40~45/38~42 |
A+C/B Mix ratio (By weight) | 100/106~108 |
Cream Time (s) | 8~10 |
End of Rise Time (s) | 50~60 |
Free Rise Foam Density(g/cm3) | 0.26~0.29 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 5~7 |
Molded Density (g/cm3) | 0.55~0.70 |
Hardness (Shore A ) | 65~72 |
Tensile strength (MPa) | 8.5~10 |
Polyether -polyurethaan schoenensysteem
Materiaalnaam: XC-7160/XC-8260
Kenmerk:
Koude weerstand Medium Hardheid Sole, Marine Fender,
schokabsorptie na coating
Sollicitatie:
Koude weerstand Medium Hardheid Sole, Marine Fender, schokabsorptie
Typische eigenschappen van PU -matrix
Characteristic: Good handle, hydrolysis resistance and cold resistance, high elasticity |
|||||||
Application: Cold resistance medium hardness sole, marine fender, shock absorption mat |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
||
A-7160 |
Liquid |
1000~1400 |
1.01~1.02 |
18 |
|||
B-8260 |
Yellowish transparent liquid or waxy |
700~1100 |
1.08~1.2 |
20 |
|||
Materials preheat |
|||||||
A-7160: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-8260: preheated at 50~60℃ for 10~12 hours. |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/106~108 |
8~10 |
50~60 |
0.26~0.29 |
45~55 |
5~7 |
The adding content of C-2 should be 250g±10g/18kg. |
|||||||
The adding content of water should be 0~40g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Flexing resistance |
/ |
Physical properties |
0.55~0.70 |
65~72 |
8.5~10 |
500~680 |
34~45 |
40,000 times no increasing |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
PU -systeem voor schoenzool, lijm voor schoenen, CPU, TPU, polyester polyol, PU -hars voor inkt, pur hot smelt lijm, lijm voor flexibel pakket, pu hars voor synthetisch leer
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.